RESUMO
Hysteresis loops exhibited by the thermal properties of undoped and 0.8 at.% W-doped nanocrystalline powders of VO2 synthesized by means of the solution combustion method and compacted in pellets, are experimentally measured by photothermal radiometry. It is shown that: (i) the W doping reduces both the hysteresis loops of VO2 and its transition temperature up to 15 °C. (ii) The thermal diffusivity decreases (increases) until (after) the metallic domains become dominant in the VO2 insulating matrix, such that its variation across the metal-insulation transition is enhanced by 23.5% with W-0.8 at.% doping. By contrast, thermal conductivity (thermal effusivity) increases up to 45% (40%) as the metallic phase emerges in the VO2 structure due to the insulator-to-metal transition, and it enhances up to 11% (25%) in the insulator state when the local rutile phase is induced by the tungsten doping. (iii) The characteristic peak of the VO2 specific heat capacity is observed in both heating and cooling processes, such that the phase transition of the 0.8 at.% W-doped sample requires about 24% less thermal energy than the undoped one. (iv) The impact of the W doping on the four above-mentioned thermal properties of VO2 mainly shows up in its insulator phase, as a result of the distortion of the local lattice induced by the electrons of tungsten. W doping at 0.8 at.% thus enhances the VO2 capability to transport heat but diminishes its thermal switching efficiency.
RESUMO
The transient changes in resistances of Cr0.8Fe0.2NbO4 thick film sensors towards specified concentrations of H2, NH3, acetonitrile, acetone, alcohol, cyclohexane and petroleum gas at different operating temperatures were recorded. The analyte-specific characteristics such as slopes of the response and retrace curves, area under the curve and sensitivity deduced from the transient curve of the respective analyte gas have been used to construct a data matrix. Principal component analysis (PCA) was applied to this data and the score plot was obtained. Distinguishing one reducing gas from the other is demonstrated based on this approach, which otherwise is not possible by measuring relative changes in conductivity. This methodology is extended for three Cr0.8Fe0.2NbO4 thick film sensor array operated at different temperatures.
RESUMO
Several research groups have attempted to optimize photopolymerization parameters to increase the throughput of scanning based microstereolithography (MSL) systems through modified beam scanning techniques. Efforts in reducing the curing line width have been implemented through high numerical aperture (NA) optical setups. However, the intensity contour symmetry and the depth of field of focus have led to grossly non-vertical and non-uniform curing profiles. This work tries to review the photopolymerization process in a scanning based MSL system from the aspect of material functionality and optical design. The focus has been to exploit the rich potential of photoreactor scanning system in achieving desired fabrication modalities (minimum curing width, uniform depth profile, and vertical curing profile) even with a reduced NA optical setup and a single movable stage. The present study tries to manipulate to its advantage the effect of optimized lower [c] (photoinitiator (PI) concentration) in reducing the minimum curing width to ~10-20 µm even with a higher spot size (~21.36 µm) through a judiciously chosen "monomer-PI" system. Optimization on grounds of increasing E(max) (maximum laser exposure energy at surface) by optimizing the scan rate provides enough time for the monomer or resin to get cured across the entire resist thickness (surface to substrate ~10-100 µm), leading to uniform depth profiles along the entire scan lengths.